Concrete reinforced with steel is the
foundation of our modern society. Reinforcement within concrete creates a composite
material, with the concrete providing strength against compressive stress while the reinforcement
provides strength against tensile stress. But, while steel reinforcement solves one
of concrete’s greatest limitations, it creates an entirely new problem: Corrosion of embedded
steel rebar is the most common form of concrete deterioration. So what are we doing about it? Hey I’m Grady, and this is Practical Engineering. On today’s episode, we’re testing out
some innovations in concrete reinforcement. Although unprotected steel is naturally prone
to corrosion, or rusting, when it gets embedded into concrete, certain factors usually work
to protect it. First is the obvious protection of simply
being shielded from the outside environment by a relatively impermeable and durable material. Water and contaminants usually can’t make
their way through the concrete to the steel. The second form of protection is the alkaline
environment. The high pH of normal concrete creates a thin
oxide layer on the steel that provides protection from corrosion. But, in some cases, this protection isn’t
enough. One of the main sources of corrosion to rebar
is salt. Whether through exposure to saltwater near
a marine environment or application of deicing salts to make roadways safer during the winter,
these chloride ions can make their way through the concrete, corroding the steel reinforcement. And when steel corrodes, it creates iron oxide
that expands inside the concrete. This expansion generates stress, sometimes
called oxide jacking, and is the one of the primary causes of concrete deterioration. So, how do we prevent these chloride ions
and other contaminants from reaching the steel and causing corrosion? The first line of defense is cover. Cover is the minimum distance between the
outside surface of the concrete and the reinforcing steel. And, depending on exposure and application,
certain codes specify different amounts of concrete cover, generally between 25 and 75
millimeters or 1 to 3 inches. Cover is one of the reasons good concrete
work takes so much effort before the concrete ever shows up on the job site. Installing strong formwork and lots and lots
of wire tying all the reinforcement together help to make absolutely sure that, through
all the jostling and walking over and general chaos that comes when it’s time to actually
place concrete, the rebar stays where it was designed to be embedded within the final product. Neglecting these steps can cause rebar to
sink to the bottom of a slab or come too close to an outside surface before the concrete
cures, eventually leading to premature corrosion of the reinforcement due to lack of cover. But, even with adequate cover, a crack in
the concrete can allow contaminants and water into direct contact with the reinforcement. And it won’t surprise you to learn that
cracks in concrete aren’t all that rare. Most concrete shrinks as it cures which can
lead to cracks. Changes in temperature also cause expansion
and contraction which can lead to cracking. Concrete can also crack under normal, expected
loading conditions due to the way the steel takes up stresses within the material. One way to solve this issue is by prestressing
the rebar, a topic I discussed briefly in a previous video and something I’d like
to dive deeper into in the future. But today I want to show another option for
reducing these cracks. Fiber reinforced concrete is pretty much exactly
what you’d expect it be. It’s not a new idea by any means, but our
understanding and use of different kinds of fibers within a concrete mix continues to
grow. Adding glass, steel, or synthetic fibers to
concrete can provide a lot of benefits, but one of the most important is crack control. I constructed three nearly identical reinforced
concrete beams to show how this works, and I let them cure for about a week. The first one only has steel rebar as reinforcement. I’m using my hydraulic press to test out
the strength of each beam and see how it performs prior to failure. And I’m using tons as a measurement of force
on these beams, just because that’s what the gauge says, but the units are completely
arbitrary to the demo. If you prefer SI, just pretend these are metric
tonnes. As I increase the load on the beam, you see
cracks starting at only around 3 tons. These cracks form because steel stretches
a little bit as it takes up the tensile stress in the concrete. The beam is holding the load just fine and
isn’t even close to failure, but concrete can’t stretch along with the steel so it
has to crack. You can imagine how these cracks could let
water and air into contact with the reinforcement and eventually deteriorate the concrete. Those cracks are the important part of this
demo, but I went ahead and increased the load until the beam failed because, hey, that’s
what hydraulic presses are good for right? For these next two beams, I included fibers
in the concrete mix: one beam has steel fibers and the other has glass fibers. The steel rebar and fibers team up to resist
tensile stresses in the beams. The rebar provides large scale reinforcement
to resist tension across the entire structural member, and the fibers provide small scale
reinforcement to resist localize tension that causes cracking. When I load these beams to 3 tons, you can’t
see a single crack. In fact, for both of these beams, I didn’t
see any cracks form until almost double that. and even then the cracks were much smaller. Both beams failed at about the same load as
first, one, which I expected. Like I said, the fibers don’t really add
much overall strength to the beam, but you can easily see they could go a long way in
preventing corrosion of steel rebar. You may be wondering why are we even using
steel for reinforcement at all? Steel is relatively inexpensive, well-tested,
and strong, but there are lots of other materials that with excellent mechanical properties
that don’t face this issue of corrosion. For very corrosive environments, we sometimes
use epoxy-coated rebar or even stainless steel, but there are some emerging alternatives like
Fiber Reinforced Polymers or FRP bars. This is reinforcement made of basalt, remelted
volcanic rock forced through tiny nozzles to create fibers that are extremely strong. Options like this often cost cost more than
steel rebar, in some cases a lot more. But, the major impediment to the use of these
newer, more innovative types of reinforcement isn’t just the cost. It’s easy to see that those additional costs
may be offset by the increased lifespan of the concrete. Another inhibition comes simply from the lack
of widespread use. Innovation happens slowly in civil engineering
because the consequences of failure are so high. Gaining confidence in a design has as much
to do with engineering theory as it does to simply seeing how well similar designs have
performed in the past. But many engineering disasters have come not
at the expense of bad design, but actually bad maintenance, so long-term durability can
be just as important to public safety as other design criteria. We’ll certainly be seeing more innovative
ways to reinforce concrete in the future, including the options I mentioned in this
video. Thank you for watching, and let me know what
you think!